Tin has probably been a part of your life since the time you first saw the Tin Man in the Wizard of Oz as a child. Of course, the use of tin extends well beyond the creation of a fictional movie character ' it has many practical applications in our daily lives. We're all familiar with tin cans that are used for holding many types of food and beverages; these containers are actually manufactured from sheet steel that is coated with a thin layer of tin known as tinplate.
Link to Ruisite
Today, roughly half of all tin produced is used in soldering applications. Tin is also used in the production of pewter, bronze and phosphorous bronze. Tin salts are sometimes sprayed onto windshields and window glass to provide an electrically conductive coating. The window glass itself is often made by floating molten glass onto molten tin, which produces a flat surface. The metal used to manufacture bells is often a combination of bronze and tin. Additionally, tin and tin alloys offer tremendous value for electroplating, which is the process of depositing a coating of metal onto the surface of a material via an electrical current.
Tin is a soft, malleable, silvery-white metal that is available in abundance throughout many parts of the world. The extraction of tin dates back to around B.C. during the Bronze Age. Bronze is a yellowish-brown alloy of copper and tin that typically consists of about one-third tin. The earliest bronze objects were found to contain a small tin component.
The Chinese began to engage in the practice of tin mining around 700 B.C. Today, tin can be found in China, Thailand and Indonesia, and it is also mined in Brazil, Peru and Bolivia. Tin is obtained by carbothermic reduction of the oxide ore, which is produced by heating the ore in a furnace.
Other key tin facts:
Why is tin such a popular choice for electroplating? Perhaps the biggest reason is that tin plating ' or 'tinning' ' is an extremely cost-effective process. Because tin is so readily available, it is much less expensive than pricier metals such as gold, platinum or palladium. Tin also offers excellent solderability, as well as superior protection against corrosion.
Tin plating can produce a whitish-gray color that is preferable when a dull or matte appearance is desired. It can also produce a shiny, metallic look when a bit more luster is preferred. Tin offers a decent level of conductivity, making tin plating useful in the manufacturing of various electronic components. Tin is also FDA approved for use in the food service industry.
The benefits listed above make tin the metal of choice for plating applications in a wide range of industries including:
Sharretts Plating services many of these industries, contact us today for a free quote!
There are three basic types of tin plating, each of which relies on the deposition of an electrolytic tin solution onto the surface of a metal object:
Tin can be electrodeposited onto just about any type of metal. Let's take a closer look at the specific components of an effective tin plating process:
1. Cleaning: It is vital to purify the substrate ' the part that receives the tin coating ' prior to immersion into the plating bath. Cleaning removes oil, grease and other surface contaminants that can reduce the effectiveness of the plating process.
Cleaning is a multi-step process that can vary somewhat depending on the composition of the substrate and the amount of grime and debris that it contains, as well as the types of cleaning equipment available for use. In general, the cleaning process includes:
2. Preparing the Plating Bath
The next step is to prepare an electrolytic solution, also known as a plating bath. Electrolytic tin plating baths can be comprised of acid tin, alkaline tin or methyl sulphonic acid solutions. A plating bath includes tin that is dissolved to form positively charged ions that are suspended in the solution, as well as other chemical additives. The bath serves as the conductive medium during electrodeposition.
Acid baths tend to be used with greater frequency, because they result in a higher deposition rate. However, while acid baths generally provide a uniform coating, they do not always reach holes or other surface irregularities with a high level of consistency.
3. The Electrodeposition Procedure
Once the substrate has been clean and immersed in the electrolyte bath, it is ready for electrodeposition of the tin coating. The object is typically placed in the center of the specially designed tank that contains the electrolytic solution. The object serves as the cathode, which is the negatively charged electrode in the electrical circuit. The anodes, which are the positively charged electrodes in the circuit, are placed near the edge of the plating tank.
The next step is to introduce a low-voltage DC current into the plating bath. A device known as a rectifier is used to convert AC power to the DC current. The introduction of the electrical current ultimately causes positively charged ions at the anode to flow through the electrolyte in the plating bath toward the negatively charged cathode (substrate), where they are electrodeposited onto the surface. The current then flows back toward the anode to complete the circuit.
4. Post Electroplating Process
Post-treatment is usually not required at the conclusion of the tin plating process. Passivation ' which is the application of a light coating of protective material ' may be used in special plating applications to provide additional corrosion protection or enhance the reactive properties of the tin. Heat treatment may also be used to prevent hydrogen embrittlement, which is a weakening of metal caused by exposure to hydrogen.
A number of issues can occur during the tin plating process that can negatively impact the final outcome. These include:
One way to enhance the tin plating process is by co-depositing (alloying) tin with another metal or several metals. Commonly applied tin alloys include:
If tin whiskers are a concern in your manufacturing environment, then you should strongly consider a tin-lead plating alloy. Unlike pure tin, as previously mentioned, tin-lead can be effective at preventing formation of whiskers, making it an excellent choice in the manufacturing of electronic components such as printed circuit boards, connectors and semiconductors. Because both metals feature a high hydrogen overvoltage, the deposition of a tin-lead alloy can be produced via strong acid solutions without the addition of complexing agents.
In addition to whisker reduction, a tin-alloy can offer greater protection against corrosion than pure tin alone. Tin-lead also provides excellent solderability and can produce a softer, more ductile finish. Because of its ductility, tin-lead can prevent damage to the underlying metal during rigorous manufacturing processes such as stamping.
Sharretts Plating Company has been in business since . Over the course of nine decades, we have developed and perfected an effective and affordable tin plating process that can be customized to your specific operating requirements. In addition to pure tin plating, we also offer an innovative tin-lead plating process that can significantly reduce the formation of tin whiskers on your electronic components.
Contact us today to learn more about our tin plating process and how it can be tailored to your operation. We'll also be happy to schedule a tin plating consultation and provide a free, no-obligation quote.
A great way to keep up with the latest tin plating developments is to sign up to receive free monthly emails from SPC. They contain lots of useful information about plating and the metal finishing industry in general.
I sometimes get questions about the basics of a process, and I receive one from a person recently hired by a job shop doing alkaline tin plating.
The following information on alkaline tin plating has been gleaned from numerous literature sources over the years.
For more Tin plating processinformation, please contact us. We will provide professional answers.
Tin is a very soft, conductive metal with a relatively low level of specific resistance.
Tin has a relatively low melting point. When applied over parts that are intended for use at high temperatures, tin can diffuse into base materials such as copper and brass. If the parts are stressed, a phenomenon called 'liquid metal embrittlement' can cause a stress fracture. For this reason, tin coatings are not recommended for fasteners made of steel, copper, copper alloys, aluminum, magnesium, or titanium and for serving at high temperatures, such as those that might be encountered in an automotive engine compartment (350°F).
Tin can exist in two crystal structures, β or body-centered tetragonal, and α, a cubic structure. Above about 13°C (55°F), tin exists in the tetragonal β crystal structure, and the metal has a density of 7.29 g/cm3. Below 13°C, the tin may undergo a transformation to the α form that is essentially non'metallic and much less dense (5.73 g/cm3). This form of tin may be called alpha-tin, gray-tin, or 'tin-pest.'
The initiation of this transformation is very slow to begin, so it is rare to encounter alpha tin, even when it is exposed at, and somewhat below, 13°C, but at much lower temperatures (~ -40°C) and over prolonged exposure at very low temperatures, once the transformation begins, alpha-tin may be visible within a few hours. This tin is dark, powdery, non-conductive and non-adherent.
Photo above courtesy of Techmetals
The formation of tin pest can be eliminated by plating an alloy containing 0.20.3% bismuth, antimony or thallium.
Because tin is non-toxic, inert to many foods, and is easy to solder, it has widespread use in the food storage and food processing industry. In addition, tin deposits are used in various household appliances. Such deposits are also used extensively for coating wire products and for bearing surfaces, as well as in a variety of electronic applications.
Generally, tin is employed due to its excellent ductility, resistance to corrosion, and solderability. The majority of tin consumed is used to coat steel to enhance corrosion resistance and provide solderability. In electronic applications, tin deposits are used to enhance solderability and as an etch resist during the manufacture of printed wiring boards, as well as for the prevention of base metal tarnishing. Tin is widely used in electronic applications, including but not limited to components, printed circuit board coatings, semiconductor devices, connectors, etch resistors during printed wiring board manufacture, etc. Pure tin coatings from plating solutions containing additives such as brighteners are prone to whisker growth. Tin deposits from alkaline solutions do not have this problem. Tin whiskers can be prevented by plating a small percentage (0.3-1.0%) of bismuth with the tin.
Tin is used for food processing and shipping containers (e.g., 'tin' cans), bearing surfaces, piping, wire coating, etc., to name a few applications. In addition, tin alloyed with other metals, such as antimony, zinc, or copper, is used to form deposited alloys that have certain desirable chemical, electrical, and/or mechanical properties for specific applications. Lead and tin-lead plating are no longer in favor because of the toxicity of lead and because the European Union (EU) has banned the importation of lead-containing coatings and products used in automotive and electronic applications.
An old term relating to tin plating thickness on steel sheets is a 'base box.' This is 112 sheets of steel, with dimensions of 20 in. x 14 in. = 31,360 in.2 of sheet or 62,720 in.2 of total surface area. Tin plating thickness is then referenced by pounds per base-box. 0. in. (2.5 m) = 1.625 pounds/basebox, for example.
Most commercial alkaline tin plating solutions are formulated with potassium salts. Potassium solutions deliver higher plating efficiencies at all normal operating temperatures vs. sodium based solutions.
The drop in cathode current efficiency as the current density is increased is confirmation that these solutions will deliver excellent throwing power, allowing for more uniform deposits over complex shapes.
Experience has shown that higher alkalinity content (caustic and carbonate) favor higher throwing power.
The stannate salts are part of the formulation in order to provide soluble tetravalent tin ions for reduction at the cathode. Variations in the concentration typically do not have a great effect on the operational characteristics of the solution. For normal plating current density range of 30'50 A/ ft2, a typical tin concentration is 42 g/L or about 5.5 oz/gal.
For plating at higher current densities, the concentration of tin is typically increased to as much as 300 g/L, at which current densities as high as 500 A/ft2 may be employed. For these solutions, the potassium formulation is a must.
Commercial versions of stannate salts typically contain moisture, alkali, and carbonate, so the yield of tin may not be the theoretical percentages. Potassium stannate contains about 38.5% tin.
The sodium or potassium hydroxide (1'3 oz/gal) is more important to control than the tin content, as it has a multitude of functions, including providing the conductivity of the solution, anode corrosion, and stabilizing the solution against hydrolysis of the tin or formation of stannite by reaction with carbon dioxide. For barrel plating, higher concentrations of alkali are typically required than for rack plating.
The free alkali content of the plating solution is critical to successful plating from this solution. It should be analyzed and adjusted daily, even if the solution is not in use, as alkali may be consumed by reaction with carbon dioxide in the air. Idle tanks should be covered with a lid or plastic sheeting. The free alkali can be lowered by the addition of a 10% volume of acetic acid. Acetic acid lowers free potassium hydroxide in a weight ratio that is close to 1:1.
The current density range is typically 30'100A/ft2 for non-barrel plating and depends heavily upon the level of agitation, temperature, and alkali content. Excess current density may produce nodules or rough deposits in the absence of adequate agitation or a temperature that is too low. Operational voltage tends to be in the 4'6 volt range, while barrel plating may require as much as 12 volts.
The operational temperature should be a minimum of 140°F (60°C). The high end of the range is not critical. At too low a temperature, the solution drops off dramatically in cathode efficiency, and rough deposits may be obtained. Normal cathode current efficiency is 60%'90%.
Operating stannate tin plating solutions are typically straw color or cloudy and tend to generate sludge as they age. This sludge tends to be slimy and colloidal, making filtration a difficult proposition. Most platers allow the sludge to settle and remove it during annual tank maintenance. Sludge production is reduced when de-ionized water is used instead of tap-water. This sludge contains a significant amount of tin. Large facilities may use reclaimers to regain lost value from the sludge.
The stannate tin solution can tolerate high concentrations of carbonate without major operational problems. The carbonate is typically allowed to reach equilibrium with the drag-out rate. The solution is also very tolerant of heavy metal impurities, with the exception of antimony, which can cause a streaky deposit in low current density areas. Low current density dummying may remove it below harmful concentrations.
Stannous tin (stannite) is a contaminant in a stannate solution. It can break down to produce sludge by forming colloidal tin. The presence of stannite may also produce rough, spongy deposits.
A spot test for detecting this ion can be performed whenever stannite is suspected to be present.
Prepare the spot test solution by dissolving 5 grams of bismuth oxide or carbonate in 100 mL of 25% vol. hydrochloric acid. Add sodium hydroxide until the solution is alkaline, and then dilute to 250 mL. Add 10 mL of the hot (180°F) plating solution to 5 mL of the spot solution. Production of dark precipitate is an indication of the presence of stannite.
To convert stannite back to stannate, dilute a small amount of hydrogen peroxide with water to make a 10% solution. Add this to the plating tank with a lot of agitation. After the addition of the peroxide, the plating solution will need to be dummied until the excess peroxide is converted to water.
It is important that the anodes dissolve as stannate (quadrivalent) ions. Proper anode filming can be achieved by using dummy parts and raising the anode current density (voltage) until the voltage increases very rapidly and the anode develops a yellow-green film. At this stage, the anode begins to dissolve as the stannate ion. After the yellow-green film forms on the anode, the current density should then be lowered to about 80 percent of the maximum value and operated in this range (along the 'final curve' in the above diagram). The yellow-green color must be maintained for the anode to operate properly.
Too low an anode current density will result in the development of a gray color film, indicating that stannite tin is dissolving. Increasing the anode current density beyond that needed to generate the yellow-green color or not turning the voltage back to 80% of that which produced the green film will turn the film black, thus passivating the anode and causing no tin to dissolve.
An alternate method of anode filming is to remove all anodes and load the tank with dummies. Apply a voltage that yields twice the normal plating current and introduce the anodes one by one until all the anodes have been filmed. Then, the voltage is reduced to yield the normal plating current density, and the dummies are replaced one by one with parts. To maintain proper anode current density, partial tank loads must be avoided, and in the case of automated plating equipment, dummies may need to be plated until a full load is present in the tank.
Frank Altmayer is a Master Surface Finisher, an AESF Fellow, and the technical education director of the AESF Foundation and NASF. He owned Scientific Control Laboratories from to and has over 50 years of experience in metal finishing. He received the AESF Past Presidents Award, NAMF Award of Special Recognition, AESF Leadership Award, AESF Fellowship Award, Chicago Branch AESF Geldzahler Service Award, and NASF Award of Special Recognition.